High-Strength Heat-Shrink Tubing
With excellent resistance to tears and cuts, this tubing withstands demanding use. It also resists chemicals. FEP tubing is more chemical resistant than PVDF tubing, and withstands higher temperatures.
SAE AMS-DTL-23053/8 and SAE AMS-DTL-23053/11 tubing meets requirements for material quality.
Dielectric strength is the maximum voltage a material can handle before it starts to breakdown. The higher the dielectric strength of a material, the better it is for preventing electricity, heat, or signal from dissipating from wire and cable.
For technical drawings and 3-D models, click on a part number.
- Shrink Ratio: See Table
- Dielectric Strength: 2,000 V/mil
- Shrink Temperature: 420° F
- Temperature Range: -400° to 400° F
- Specifications Met: SAE AMS-DTL-23053/11
ID | ||||||||
---|---|---|---|---|---|---|---|---|
Before Shrinking | Min. After Shrinking | Min. Wall Thick. After Shrinking | For Wire Gauge | For Wire Size | Color | Lengths, ft. | Per Ft. | |
1.3:1 Shrink Ratio | ||||||||
0.031" | 0.027" | 0.01" | 24 | __ | Clear | 00000000 | 00000 | |
0.036" | 0.032" | 0.01" | 22 | __ | Clear | 00000000 | 0000 | |
0.045" | 0.039" | 0.01" | 20 | __ | Clear | 00000000 | 0000 | |
0.06" | 0.049" | 0.01" | 18 | __ | Clear | 00000000 | 0000 | |
0.075" | 0.061" | 0.01" | 16 | __ | Clear | 00000000 | 0000 | |
0.092" | 0.072" | 0.01" | 14 | __ | Clear | 00000000 | 0000 | |
0.115" | 0.089" | 0.01" | 12 | __ | Clear | 00000000 | 0000 | |
0.141" | 0.114" | 0.01" | 10 | __ | Clear | 00000000 | 0000 | |
0.18" | 0.143" | 0.01" | 8 | __ | Clear | 00000000 | 0000 | |
0.225" | 0.18" | 0.01" | 6 | __ | Clear | 00000000 | 0000 | |
0.29" | 0.226" | 0.01" | 4 | __ | Clear | 00000000 | 0000 | |
0.365" | 0.28" | 0.01" | 2 | __ | Clear | 00000000 | 0000 | |
0.44" | 0.349" | 0.01" | 1/0 | __ | Clear | 00000000 | 0000 | |
0.58" | 0.448" | 0.02" | __ | 7/16" | Clear | 00000000 | 00000 | |
0.666" | 0.51" | 0.02" | __ | 1/2" | Clear | 00000000 | 00000 | |
0.83" | 0.637" | 0.03" | __ | 5/8" | Clear | 00000000 | 00000 | |
1" | 0.764" | 0.03" | __ | 3/4" | Clear | 00000000 | 00000 | |
Each | ||||||||
1.6:1 Shrink Ratio | ||||||||
0.094" | 0.056" | 0.01" | __ | 3/32" | Clear | 4 | 00000000 | 00000 |
0.125" | 0.075" | 0.01" | __ | 1/8" | Clear | 4 | 00000000 | 00000 |
0.188" | 0.115" | 0.01" | __ | 3/16" | Clear | 4 | 00000000 | 00000 |
0.25" | 0.15" | 0.01" | __ | 1/4" | Clear | 4 | 00000000 | 00000 |
0.375" | 0.235" | 0.01" | __ | 3/8" | Clear | 4 | 00000000 | 00000 |
0.5" | 0.3" | 0.02" | __ | 1/2" | Clear | 4 | 00000000 | 00000 |
- Shrink Ratio: 1.3:1
- Dielectric Strength: 1,400 V/mil
- Shrink Temperature: 350° F
- Temperature Range: -450° to 400° F
ID | ||||||||||
---|---|---|---|---|---|---|---|---|---|---|
Before Shrinking | Min. After Shrinking | Min. Wall Thick. After Shrinking | Color | 1 ft. | 2 ft. | 3 ft. | 4 ft. | 6 ft. | 8 ft. | |
1.1" | 0.88" | 0.02" | Clear | 00000000 | ||||||
1.3" | 1" | 0.02" | Clear | 00000000 | ||||||
1.7" | 1.3" | 0.02" | Clear | 00000000 | ||||||
2.1" | 1.7" | 0.02" | Clear | 00000000 | ||||||
2.6" | 2.1" | 0.02" | Clear | 00000000 | ||||||
3.1" | 2.6" | 0.02" | Clear | 00000000 | ||||||
4.3" | 3.5" | 0.02" | Clear | 00000000 | ||||||
5.2" | 4.3" | 0.02" | Clear | 00000000 | ||||||
6.2" | 5.2" | 0.02" | Clear | 00000000 |
Easy-to-Remove Heat-Shrink Tubing
- Material: Fluoropolymer Plastic
- Shrink Ratio: See Table
- Dielectric Strength: 2,000 V/mil
- Shrink Temperature: 420° F
- Temperature Range: Not Rated to 400° F
Access connections more easily than with standard heat-shrink tubing. Make a small slit in this tubing to peel it away. Made of fluoropolymer, it resists chemicals and withstands temperatures up to 400° F.
Dielectric strength is the maximum voltage a material can handle before it starts to breakdown.
Harsh Environment Heat-Shrink Tubing Assortments
Maintain a supply of tubing in a variety of sizes and materials that withstands harsh conditions such as abrasion, moisture, and chemicals.
FEP tubing is high strength to resist abrasion, cuts, tears, and chemicals.