High-Strength 7075 Aluminum Sheets and Bars
Originally developed for aircraft frames, uses for 7075 aluminum now include keys, gears, and other high-stress parts. It is often used as a replacement for 2024 aluminum because it’s stronger and provides similar performance in all other aspects.
Cold-drawn bars are formed by a die for close-tolerance widths, then cut to the lengths listed.
For technical drawings and 3-D models, click on a part number.
Certificates with a traceable lot number are available for these products. Download certificates from ORDER HISTORY after your order ships.
- Yield Strength: See Table
- Hardness: Brinell 130 (Medium)
- Temper: See Table
- Fabrication: Cold Drawn
- Specifications Met: ASTM B211, SAE AMS-QQ-A-225/9
| Wd. | Yield Strength  | Temper | Heat Treatment | Temperature Range, °F | 1/2 ft. Lg. | 1 ft. Lg. | 2 ft. Lg. | 3 ft. Lg. | 6 ft. Lg. | |
1/4" Thick. (-0.002" to 0.002" Tolerance) | ||||||||||
|---|---|---|---|---|---|---|---|---|---|---|
| 1" | 73,000 psi | T651 | Hardened | -320° to 210° | 0000000 | |||||
| 2" | 73,000 psi | T651 | Hardened | -320° to 210° | 0000000 | |||||
| 2 1/2" | 73,000 psi | T651 | Hardened | -320° to 210° | 0000000 | |||||
1/2" Thick. (-0.002" to 0.002" Tolerance) | ||||||||||
| 1" | 62,000 psi | T7351 | Hardened | -320° to 210° | 0000000 | |||||
| 1 1/2" | 73,000 psi | T651 | Hardened | -320° to 210° | 0000000 | |||||
| 2" | 62,000 psi | T7351 | Hardened | -320° to 210° | 0000000 | |||||
| 2 1/2" | 73,000 psi | T651 | Hardened | -320° to 210° | 0000000 | |||||
| 3" | 73,000 psi | T651 | Hardened | -320° to 210° | 0000000 | |||||
| 4" | 73,000 psi | T651 | Hardened | -320° to 210° | 0000000 | |||||
3/4" Thick. (-0.003" to 0.003" Tolerance) | ||||||||||
| 1" | 62,000 psi | T7351 | Hardened | -320° to 210° | 0000000 | |||||
| 2" | 62,000 psi | T7351 | Hardened | -320° to 210° | 0000000 | |||||
| 3" | 62,000 psi | T7351 | Hardened | -320° to 210° | 0000000 | |||||
1" Thick. (-0.003" to 0.003" Tolerance) | ||||||||||
| 1" | 73,000 psi | T651 | Hardened | -320° to 210° | 0000000 | |||||
| 1 1/2" | 62,000 psi | T7351 | Hardened | -320° to 210° | 0000000 | |||||
| 2" | 62,000 psi | T7351 | Hardened | -320° to 210° | 0000000 | |||||
| 2 1/2" | 62,000 psi | T7351 | Hardened | -320° to 210° | 0000000 | |||||
| 3" | 62,000 psi | T7351 | Hardened | -320° to 210° | 0000000 | |||||
1" Thick. (-0.0025" to 0.0025" Tolerance) | ||||||||||
| 4" | 62,000 psi | T7351 | Hardened | -320° to 210° | 0000000 | |||||
1 1/4" Thick. (-0.003" to 0.003" Tolerance) | ||||||||||
| 1 1/2" | 62,000 psi | T7351 | Hardened | -320° to 210° | 0000000 | |||||
| 2" | 62,000 psi | T7351 | Hardened | -320° to 210° | 0000000 | |||||
| 2 1/2" | 62,000 psi | T7351 | Hardened | -320° to 210° | 0000000 | |||||
| 3" | 62,000 psi | T7351 | Hardened | -320° to 210° | 0000000 | |||||
1 1/2" Thick. (-0.003" to 0.003" Tolerance) | ||||||||||
| 1 1/2" | 62,000 psi | T7351 | Hardened | -320° to 210° | 0000000 | |||||
| 2" | 62,000 psi | T7351 | Hardened | -320° to 210° | 0000000 | |||||
| 2 1/2" | 62,000 psi | T7351 | Hardened | -320° to 210° | 0000000 | |||||
| 3" | 62,000 psi | T7351 | Hardened | -320° to 210° | 0000000 | |||||
| 4" | 62,000 psi | T7351 | Hardened | -320° to 210° | 0000000 | |||||
2" Thick. (-0.005" to 0.005" Tolerance) | ||||||||||
| 2" | 62,000 psi | T7351 | Hardened | -320° to 210° | 0000000 | |||||
| 2 1/2" | 62,000 psi | T7351 | Hardened | -320° to 210° | 0000000 | |||||
| 3" | 62,000 psi | T7351 | Hardened | -320° to 210° | 0000000 | |||||
| 4" | 62,000 psi | T7351 | Hardened | -320° to 210° | 0000000 | |||||
2 1/2" Thick. (-0.008" to 0.008" Tolerance) | ||||||||||
| 2 1/2" | 62,000 psi | T7351 | Hardened | -320° to 210° | 0000000 | |||||
| 3" | 62,000 psi | T7351 | Hardened | -320° to 210° | 0000000 | |||||
3" Thick. (-0.008" to 0.008" Tolerance) | ||||||||||
| 3" | 62,000 psi | T7351 | Hardened | -320° to 210° | 0000000 | |||||
| 4" | 62,000 psi | T7351 | Hardened | -320° to 210° | 0000000 | |||||
High-Strength 7075 Aluminum Rods and Discs
Originally developed for aircraft frames, uses for 7075 aluminum now include keys, gears, and other high-stress parts. It is often used as a replacement for 2024 aluminum because it’s stronger and provides similar performance in all other aspects.
For technical drawings and 3-D models, click on a part number.
Certificates with a traceable lot number are available for these products. Download certificates from ORDER HISTORY after your order ships.
- Yield Strength: 73,000 psi
- Hardness: Brinell 150 (Medium)
- Temper:
3/8" to 5/8" dia.: T6
All other sizes: T651 - Fabrication: Cold Drawn
- Specifications Met: ASTM B211, SAE AMS-QQ-A-225/9
| Dia. | Dia. Tolerance | Heat Treatment | Temperature Range, °F | 1/2 ft. Lg. | 1 ft. Lg. | 2 ft. Lg. | 3 ft. Lg. | 6 ft. Lg. | |
| 3/8" | -0.002" to 0.002" | Hardened | -320° to 210° | 00000000 | |||||
| 1/2" | -0.002" to 0.002" | Hardened | -320° to 210° | 00000000 | |||||
| 5/8" | -0.002" to 0.002" | Hardened | -320° to 210° | 00000000 | |||||
| 3/4" | -0.002" to 0.002" | Hardened | -320° to 210° | 00000000 | |||||
| 7/8" | -0.002" to 0.002" | Hardened | -320° to 210° | 00000000 | |||||
| 1" | -0.002" to 0.002" | Hardened | -320° to 210° | 00000000 | |||||
| 1 1/8" | -0.003" to 0.003" | Hardened | -320° to 210° | 00000000 | |||||
| 1 1/4" | -0.003" to 0.003" | Hardened | -320° to 210° | 00000000 | |||||
| 1 3/8" | -0.003" to 0.003" | Hardened | -320° to 210° | 00000000 | |||||
| 1 1/2" | -0.003" to 0.003" | Hardened | -320° to 210° | 00000000 | |||||
| 1 5/8" | -0.004" to 0.004" | Hardened | -320° to 210° | 00000000 | |||||
| 1 3/4" | -0.004" to 0.004" | Hardened | -320° to 210° | 00000000 | |||||
| 1 7/8" | -0.004" to 0.004" | Hardened | -320° to 210° | 00000000 | |||||
| 2" | -0.004" to 0.004" | Hardened | -320° to 210° | 00000000 | |||||
| 2 1/8" | -0.006" to 0.006" | Hardened | -320° to 210° | 00000000 | |||||
| 2 1/4" | -0.006" to 0.006" | Hardened | -320° to 210° | 00000000 | |||||
| 2 3/8" | -0.006" to 0.006" | Hardened | -320° to 210° | 00000000 | |||||
| 2 1/2" | -0.006" to 0.006" | Hardened | -320° to 210° | 00000000 | |||||
| 2 5/8" | -0.006" to 0.006" | Hardened | -320° to 210° | 00000000 | |||||
| 2 3/4" | -0.006" to 0.006" | Hardened | -320° to 210° | 00000000 | |||||
| 3" | -0.006" to 0.006" | Hardened | -320° to 210° | 00000000 | |||||
| 3 1/4" | -0.008" to 0.008" | Hardened | -320° to 210° | 00000000 | |||||
| 3 1/2" | -0.012" to 0.012" | Hardened | -320° to 210° | 00000000 | |||||
| 3 3/4" | -0.012" to 0.012" | Hardened | -320° to 210° | 00000000 | |||||
| 4" | -0.012" to 0.012" | Hardened | -320° to 210° | 00000000 | |||||
| 4 1/2" | -0.012" to 0.012" | Hardened | -320° to 210° | 00000000 | |||||
| 5" | -0.012" to 0.012" | Hardened | -320° to 210° | 00000000 | |||||
| 6" | -0.016" to 0.016" | Hardened | -320° to 210° | 00000000 |
High-Strength 7075 Aluminum Hex Bars
- Yield Strength: 56,000 psi
- Hardness: Brinell 125 (Medium)
- Temper: T7351
- Fabrication: Cold Drawn
- Specifications Met: ASTM B211, SAE AMS-QQ-A-225/9
Originally developed for aircraft frames, uses for 7075 aluminum now include shafts, gears, and other high-stress parts. It is often used as a replacement for 2024 aluminum because it’s stronger and provides similar performance in all other aspects.
For technical drawings and 3-D models, click on a part number.
Certificates with a traceable lot number are available for these products. Download certificates from ORDER HISTORY after your order ships.