Scratch- and UV-Resistant Acrylic Balls
- Color: Clear
- Max. Temperature: See table
- Tensile Strength: See table
- Impact Strength: 0.040 ft.-lbs./in. (Poor)
- Hardness: See table
- For Use Outdoors: Yes
- Specifications Met: UL 94 HB
A lightweight alternative to glass balls, acrylic balls maintain clarity over time. They are scratch and UV resistant, so they stand up to outdoor use better than polycarbonate.
For technical drawings and 3-D models, click on a part number.
| Dia. | Dia. Tolerance | Maximum Temperature, °F | Tensile Strength | Hardness | Pkg. Qty. | Pkg. | |
Semi-Clear | |||||||
|---|---|---|---|---|---|---|---|
| 1/16" | -0.002" to 0.002" | 180° | 9,195-11,030 psi (Good) | Rockwell M89-M96 (Hard) | 500 | 0000000 | 000000 |
| 1/8" | -0.002" to 0.002" | 180° | 9,195-11,030 psi (Good) | Rockwell M89-M96 (Hard) | 250 | 0000000 | 00000 |
| 3/16" | -0.002" to 0.002" | 180° | 9,195-11,030 psi (Good) | Rockwell M89-M96 (Hard) | 100 | 0000000 | 00000 |
| 1/4" | -0.002" to 0.002" | 180° | 9,195-11,030 psi (Good) | Rockwell M89-M96 (Hard) | 100 | 0000000 | 00000 |
| 3/8" | -0.002" to 0.002" | 180° | 9,195-11,030 psi (Good) | Rockwell M89-M96 (Hard) | 50 | 0000000 | 00000 |
| 1/2" | -0.002" to 0.002" | 180° | 9,195-11,030 psi (Good) | Rockwell M89-M96 (Hard) | 25 | 0000000 | 00000 |
| 5/8" | -0.002" to 0.002" | 180° | 9,195-11,030 psi (Good) | Rockwell M89-M96 (Hard) | 25 | 0000000 | 00000 |
| 3/4" | -0.002" to 0.002" | 180° | 9,195-11,030 psi (Good) | Rockwell M89-M96 (Hard) | 10 | 0000000 | 00000 |
| 1" | -0.002" to 0.002" | 180° | 9,195-11,030 psi (Good) | Rockwell M89-M96 (Hard) | 5 | 0000000 | 00000 |
Clear | |||||||
| 3/4" | -0.005" to 0.005" | 145° | 8,100 psi (Good) | Rockwell M80-M100 (Hard) | 10 | 0000000 | 00000 |
| 1" | -0.005" to 0.005" | 145° | 8,100 psi (Good) | Rockwell M80-M100 (Hard) | 5 | 0000000 | 00000 |
| 2" | -0.01" to 0.01" | 145° | 8,100 psi (Good) | Rockwell M80-M100 (Hard) | 1 | 0000000 | 00000 |